Polykemi AB POLYelast TPE Z606 Thermoplastic Elastomer, SEBS-based
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Polykemi AB |
| Trade Name | POLYelast |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYelast TPE Z606 Thermoplastic Elastomer, SEBS-based.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | With Flow; ISO 2577 |
| 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 @Time 15.0 sec |
60 @Time 0.00417 hour |
Polykemi |
| Tensile Strength at Break | <= 7.80 MPa | <= 1130 psi | ISO/R527 |
| Elongation at Break | 700 % | 700 % | ISO/R527 |
| 100% Modulus | 0.00180 GPa | 0.261 ksi | ISO/R527 |
| 300% Modulus | 0.00320 GPa | 0.464 ksi | ISO/R527 |
| Tear Strength | 30.0 kN/m | 171 pli | D624 |
| Compression Set | 20 % @Temperature 23.0 °C, Time 259000 sec |
20 % @Temperature 73.4 °F, Time 72.0 hour |
DIN 53517 |
| 45 % @Temperature 70.0 °C, Time 86400 sec |
45 % @Temperature 158 °F, Time 24.0 hour |
DIN 53517 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | Low | % of injection pressure |
| Injection Pressure | Low | |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Perstorp Compounds AMITEC 751 Melamine
- Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours
- Gromax BTE45-DN00N1 Nylon 6 (Conditioned)
- Saint-Gobain CHR® 2302-20R UHMW Film Backing Acrylic Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Blue 4012 Concentrate Based in Polyethylene
- Tipco Tipcolene® CR 6216 - 40% Talc/Mineral Reinforced Polypropylene Copolymer Compound with Controlled Rheology
- Diamond Polymers NPP30-0500 Homopolymer Polypropylene
- Arlon R37732W079 0.079" (2.01 mm) Cured Silicone Rubber with Treated FEP Film Substrate
- Lubrizol Estane® T865A Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved