SABIC Innovative Plastics LNP Verton MX03017 PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Verton MX03017 PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* MX03017 is a compound based on Polypropylene resin containing Glass Fiber, Long Glass Fiber. Added features of this material include: Chemically Coupled.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| 1.35 g/cc | 0.0488 lb/in³ | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | ASTM D 638 |
| 141 MPa | 20500 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D 638 | |
| Tensile Modulus | 10.44 GPa | 1514 ksi | 50 mm/min; ASTM D 638 |
| 13.87 GPa | 2012 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D 790 |
| 214 MPa | 31000 psi | ISO 178 | |
| Flexural Modulus | 9.34 GPa | 1350 ksi | ASTM D 790 |
| 11.15 GPa | 1617 ksi | ISO 178 | |
| Izod Impact, Notched | 2.08 J/cm @Temperature 23.0 °C |
3.90 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 66.0 kJ/m² @Temperature 23.0 °C |
31.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 13.0 J | 9.59 ft-lb | Multiaxial Impact; ISO 6603 |
| 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 93.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 45.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 94.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
52.5 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Europe-Africa-Middle East)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 305ºF Cure Temperature
- 3M Dyneon™ TF 4246 PTFE 35% Electrocarbon Filled (discontinued **)
- Karina Polar Clear PVC Compound
- Lanxess Durethan® DP BM 410 H2.0 901510 Nylon 6, 10% Mineral + Glass Fiber
- Techmer ES HiFill® PA4/6 CF40 HS 40% Carbon Filled (Dry)
- Cossa Polimeri ESTAPROP KUR 0550 V0 HF Flame Retardant Polypropylene
- 3M Scotch-Weld™ 1838L B/A Two-Part Structural Adhesive
- Axiall 1651 Clear 7002 Flexible PVC
- Chevron Phillips Marlex® 9515H High Density Polyethylene, Blow Molding
Copyright © lookpolymers.com All Rights Reserved