PolyOne Versollan™ RU 2204X Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versollan™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versollan™ RU 2204X Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versollan™ RU 2204X is the first of a new class of high performance, injection moldable TPU alloys developed to offer a rubbery feel and appearance, reduced cycle times, combined with the performance properties associated with TPUs. - Bonds to PC, ABS, PC/ABS, and Copolyester - Excellent Abrasion Resistance - Fast Set Up Rates During Processing - Good Chemical and Oil Resistance - Matte Finish - Rubbery, Soft Touch FeelColor concentrates with EVA or LDPE carrier are most suitable for coloring Versollan™ RU 2204X. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versollan™ RU 2204X with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versollan™ RU 2204X should not be left in the barrel for extended idle periods (greater than 5 minutes). Suggested Dewpoint: -40°F Injection Speed: 0.5 to 2 in/sec 1st Stage - Boost Pressure: 300 to 700 psi 2nd Stage - Hold Pressure: 30% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Viscosity 13900 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
13900 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
69000 cP

@Shear Rate 1340 1/s,
Temperature 200 °C
69000 cP

@Shear Rate 1340 1/s,
Temperature 392 °F
ASTM D3835
Maximum Moisture Content 0.020 - 0.030
0.020 - 0.030
Linear Mold Shrinkage, Flow 0.012 - 0.016 cm/cm
0.012 - 0.016 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 190 °C
11 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
76 g/10 min

@Load 5.00 kg,
Temperature 200 °C
76 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 55
55
10 sec; ASTM D2240
Tensile Strength at Break 12.4 MPa

@Temperature 23.0 °C
1800 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.86 MPa

@Strain 100 %,
Temperature 23.0 °C
270 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
3.03 MPa

@Strain 300 %,
Temperature 23.0 °C
439 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 690 %

@Temperature 23.0 °C
690 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 42.0 kN/m
240 pli
ASTM D624
Compression Set 26 %

@Temperature 23.0 °C,
Time 79200 sec
26 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Processing Properties Metric English Comments
Rear Barrel Temperature 163 - 188 °C
325 - 370 °F
Middle Barrel Temperature 182 - 193 °C
360 - 379 °F
Front Barrel Temperature 188 - 210 °C
370 - 410 °F
Nozzle Temperature 193 - 216 °C
379 - 421 °F
Melt Temperature 188 - 210 °C
370 - 410 °F
Mold Temperature 21.1 - 32.2 °C
70.0 - 90.0 °F
Drying Temperature 48.9 - 54.4 °C
120 - 130 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Back Pressure 0.000 - 0.552 MPa
0.000 - 80.1 psi
Screw Speed 75 - 125 rpm
75 - 125 rpm
Descriptive Properties Value Comments
Appearance Natural Color
Features Good Abrasion Resistance
Good Chemical Resistance
Oil Resistant
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Suggested Max Regrind 20%