PolyOne LubriOne™ NN-30CF/15T-02S black Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ NN-30CF/15T-02S black Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.33 g/cc	1.33 g/cc	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ISO 294-4
Melt Flow	3.6 g/10 min @Load 2.16 kg, Temperature 275 °C	3.6 g/10 min @Load 4.76 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	162 MPa	23500 psi	Type I, 5.0 mm/min; ISO 527
Elongation at Break	1.0 - 2.0 %	1.0 - 2.0 %	Type I, 5.0 mm/min; ISO 527
Tensile Modulus	19.1 GPa	2770 ksi	Type I, 5.0 mm/min; ISO 527
Flexural Strength	210 MPa	30500 psi	ISO 178
Flexural Modulus	13.6 GPa	1970 ksi	ISO 178
Charpy Impact Unnotched	2.10 J/cm²	9.99 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.450 J/cm²	2.14 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	260 °C	500 °F	Annealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	240 °C	464 °F	Annealed; ISO 75-2/A

Processing Properties	Metric	English
Melt Temperature	288 - 299 °C	550 - 570 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	71.1 - 82.2 °C	160 - 180 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour

Descriptive Properties	Value	Comments
Appearance	Black
Features	Electrically Conductive
	Good Wear Resistance
	High Stiffness
	Lubricated
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers