Polyram PlusTek PA309G6 Nylon 6.6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA309G6 Nylon 6.6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass fiber reinforced, UV stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | DIN 53479 |
| Water Absorption | 5.6 % | 5.6 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 175 MPa | 25400 psi | ASTM-D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM-D638 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | ASTM-D790 |
| Flexural Strength | 279 MPa | 40500 psi | ASTM D790 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous Use |
| 240 °C | 464 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | DIN 53482 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Schwartz Technical Plastics LAMIGAMID® 510 Polyethylene Terephthalate
- A. Schulman FORMION™ FI 397 Ionomer
- Polyram RamOfin PPH308G50 Polypropylene, 50% Glass Fiber, Impact Modified
- Dura-Bar 80-55-06 Continuously Cast Ductile Iron Bar Stock ASTM A536
- Colorite Polymers Flexchem 4551-02 Vinyl Compound
- BorsodChem ONGRONAT PE-191 MDI Isocyanate
- Austin Novel Materials Texalan® 664D Polyester and Polyether based TPU
- SABIC Innovative Plastics LNP Thermocomp TX88477 PU
Copyright © lookpolymers.com All Rights Reserved