PolyOne LubriOne™ NN-000/10T-2S Black Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ NN-000/10T-2S Black Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D792
Water Absorption	0.25 % @Thickness 3.18 mm	0.25 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.012 - 0.018 cm/cm	0.012 - 0.018 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	64.8 MPa	9400 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	7.0 - 18 %	7.0 - 18 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	1.79 GPa	260 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	96.5 MPa	14000 psi	ASTM D790
Flexural Modulus	2.48 GPa	360 ksi	ASTM D790
Izod Impact, Notched	0.400 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.749 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Unnotched	11.0 J/cm	20.6 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	220 °C @Thickness 6.35 mm	428 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	67.8 °C @Thickness 6.35 mm	154 °F @Thickness 0.250 in	Unannealed; ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	277 - 304 °C	531 - 579 °F

Descriptive Properties	Value	Comments
Features	Good Wear Resistance
	Low Friction
	Lubricated
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers