PolyOne Lubri-Tech™ ATH-000/20T Homopolymer Acetal - 20% PTFE Lubricated  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ ATH-000/20T Homopolymer Acetal - 20% PTFE Lubricated  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.020 cm/cm

@Thickness 3.17 mm
 0.020 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 48.0 MPa
6960 psi
ASTM D638
Elongation at Break 10 %
10 %
ASTM D638
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 6.35 mm
 0.993 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
ASTM D648
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 188 - 216 °C
370 - 421 °F
Stock
Mold Temperature 49.0 - 82.0 °C
120 - 180 °F
Drying Temperature 82.0 °C
180 °F