PolyOne Lubri-Tech™ ATH-000/02T Homopolymer - 2% PTFE  (discontinued **)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Lubri-Tech™ ATH-000/02T Homopolymer - 2% PTFE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by PolyOne.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ASTM D792
Water Absorption 0.010 %
0.010 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.010 - 0.020 cm/cm

@Thickness 3.17 mm
 0.010 - 0.020 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 59.0 MPa
8560 psi
ASTM D638
Elongation at Break 3.0 - 8.0 %
3.0 - 8.0 %
ASTM D638
Tensile Modulus 3.00 GPa
435 ksi
ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
ASTM D790
Izod Impact, Notched 0.480 - 0.800 J/cm

@Thickness 6.35 mm
 0.899 - 1.50 ft-lb/in

@Thickness 0.250 in
 ASTM D256
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Processing Properties Metric English Comments
Melt Temperature 188 - 216 °C
370 - 421 °F
Stock
Mold Temperature 60.0 - 71.0 °C
140 - 160 °F
Drying Temperature 71.0 °C
160 °F