Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg M46J Fibre

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg M46J Fibre.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
1947 - 38% resin weight with M46J 52.5% fiber volumeInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa

@Temperature 90.0 °C
 6670 psi

@Temperature 194 °F
 90º, Conditioning: 23°C; ASTM D3039
50.0 MPa

@Temperature 23.0 °C
 7250 psi

@Temperature 73.4 °F
 90º, Conditioning: 23°C; ASTM D3039
1823 MPa

@Temperature 23.0 °C
 264400 psi

@Temperature 73.4 °F
 0º, Conditioning: 23°C; ASTM D3039
Tensile Modulus 5.30 GPa

@Temperature 90.0 °C
 769 ksi

@Temperature 194 °F
 90º, Conditioning: 23°C; ASTM D3039
7.60 GPa

@Temperature 23.0 °C
 1100 ksi

@Temperature 73.4 °F
 90º, Conditioning: 23°C; ASTM D3039
213 GPa

@Temperature 23.0 °C
 30900 ksi

@Temperature 73.4 °F
 0º, Conditioning: 23°C; ASTM D3039
Flexural Yield Strength 906 MPa

@Temperature 90.0 °C
 131000 psi

@Temperature 194 °F
 0º, Conditioning: 23°C; ASTM D790
1120 MPa

@Temperature 23.0 °C
 162000 psi

@Temperature 73.4 °F
 0º, Conditioning: 23°C; ASTM D790
Flexural Modulus 191 GPa

@Temperature 90.0 °C
 27700 ksi

@Temperature 194 °F
 0º, Conditioning: 23°C; ASTM D790
199 GPa

@Temperature 23.0 °C
 28900 ksi

@Temperature 73.4 °F
 0º, Conditioning: 23°C; ASTM D790
Compressive Yield Strength 196 MPa
28400 psi
Compression After Impact @ 6.67 J/mm
965 MPa

@Temperature 23.0 °C
 140000 psi

@Temperature 73.4 °F
 0º, 120°C Cure, Conditioning: 23°C; ASTM D965
1052 MPa

@Temperature 23.0 °C
 152600 psi

@Temperature 73.4 °F
 0º, Conditioning: 23°C; ASTM D965
Shear Strength 46.0 MPa

@Temperature 60.0 °C
 6670 psi

@Temperature 140 °F
 0º Interlaminar Shear, Conditioning: 60°C-90%RH; ASTM D2344
54.0 MPa

@Temperature 90.0 °C
 7830 psi

@Temperature 194 °F
 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344
58.0 MPa

@Temperature 90.0 °C
 8410 psi

@Temperature 194 °F
 0º Interlaminar Shear, 120°C Cure, Conditioning: 23°C; ASTM D2344
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
 0º Interlaminar Shear, 120°C Cure, Conditioning: 23°C; ASTM D2344
81.0 MPa

@Temperature 23.0 °C
 11700 psi

@Temperature 73.4 °F
 0º Interlaminar Shear, Conditioning: 23°C; ASTM D2344
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature -18.0 °C
 12.0 Month

@Temperature -0.400 °F