- PolyOne Lubri-Tech™ AT-25GB/5T-2S Acetal-Copolymer, Glass Bead Filled, PTFE/Silicone Lubricated (discontinued
PolyOne Lubri-Tech™ AT-25GB/5T-2S Acetal-Copolymer, Glass Bead Filled, PTFE/Silicone Lubricated (discontinued
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-25GB/5T-2S Acetal-Copolymer, Glass Bead Filled, PTFE/Silicone Lubricated
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledPTFE/Silicone LubricatedInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.618 g/cc | 1.618 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Thickness 3.17 mm |
0.020 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0095 - 0.015 cm/cm | 0.0095 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 340 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 227 °C | 400 - 440 °F | Molding |
| Mold Temperature | 54.4 - 71.1 °C | 130 - 160 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML7647 PC (Europe-Africa-Middle East)
- KKPC KOSYN KSL 352 Styrene-Butadiene Latex
- Mitsui ADMER® SF700A Elastomer Type Polyolefin
- LATI Latamid 6 H2 G/30 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized
- MetalTek MTEK 80-10-10 Cast UNS C93700 Bearing Bronze
- Taiwan Sheen Soon Sheenthane® A8800F Thermoplastic Polyurethane Elastomer
- SABIC Innovative Plastics ULTEM DT1810EV PEI Blend
- A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene
- Axiall 8553 Moldings & Extrusions Flexible PVC
- BASF Ultraform N 2200 G53 UNC Q600 25% Glass Filled POM
Copyright © lookpolymers.com All Rights Reserved