Styron CALIBREâ„¢ 603 3 Polycarbonate, Branched

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Styron
Trade Name CALIBRE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 603 3 Polycarbonate, Branched.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CALIBRE® 603 is a branched polycarbonate resin and is equipped with a mold release and a UV stabilization package. CALIBRE 603 resins exhibit an excellent property balance of high clarity, high melt strength and impact resistance.The CALIBRE 603 resins have high zero-shear viscosity which allow extrusion of complex sheet structures for the building industry or extrusion blow molding of large products without sagging.Available Melt Flow Rates: 3, 5.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM Data
Melt Flow 3.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
3.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 64.8 MPa
9400 psi
ASTM Data
Tensile Strength, Yield 65.5 MPa
9500 psi
ASTM Data
Elongation at Break 100 %
100 %
ASTM Data
Elongation at Yield 6.0 %
6.0 %
ISO Data
Tensile Modulus 2.21 GPa
321 ksi
ASTM Data
Izod Impact, Notched 8.54 J/cm
16.0 ft-lb/in
ASTM Data
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Unannealed; ASTM Data
Vicat Softening Point 152 °C
306 °F
Flammability, UL94 V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Optical Properties Metric English Comments
Haze 1.1 %
1.1 %
Transmission, Visible 89 %
89 %