PolyOne Geon™ Vinyl Rigid Molding M5730 Natural Polyvinyl Chloride, Rigid (PVC, Rigid)

Category Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ Vinyl Rigid Molding M5730 Natural Polyvinyl Chloride, Rigid (PVC, Rigid).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NOTE: Geon weatherable compounds contain pigments and ingredients that, along with processing conditions, contribute to the weathering performance of the PVC compounds. The weathering performance of unpigmented compounds or so-called natural compounds generally is inferior to pigmented compounds. Unpigmented weatherable compounds may also contain non-pigment ingredients which can interact unpredictably with pigments to produce unexpected weathering results. Therefore, in applications where processors or customers would like to use an unpigmented compound, or add their own pigment package, it is the customer's responsibility to determine whether or not the weathering performance after pigmenting is acceptable in their specific end-use application.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 88.9 cm
35.0 in
Mechanical Properties Metric English Comments
Hardness, Shore D 79
79
15 sec; ASTM D2240
Tensile Strength, Yield 42.7 MPa
6190 psi
Type I, 51 mm/min; ASTM D638
Elongation at Break 50 %
50 %
Type I, 51 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
Type I, 51 mm/min; ASTM D638
Flexural Strength 71.0 MPa
10300 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm

@Thickness 3.18 mm,
Temperature -18.0 °C
0.993 ft-lb/in

@Thickness 0.125 in,
Temperature -0.400 °F
Injection Molded; ASTM D256A
2.70 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
5.06 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Injection Molded; ASTM D256A
4.30 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
8.06 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 73.9 °C

@Thickness 6.35 mm
165 °F

@Thickness 0.250 in
Unannealed; ASTM D648
77.8 °C

@Thickness 6.35 mm
172 °F

@Thickness 0.250 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 72.2 °C

@Thickness 6.35 mm
162 °F

@Thickness 0.250 in
Unannealed; ASTM D648
76.1 °C

@Thickness 6.35 mm
169 °F

@Thickness 0.250 in
Annealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
ALL; UL 94
5VA

@Thickness 1.91 mm
5VA

@Thickness 0.0752 in
ALL; UL 94
Processing Properties Metric English Comments
Melt Temperature 199 - 210 °C
390 - 410 °F
Descriptive Properties Value Comments
Features General Purpose
High Flow
Medium Impact Resistance
Forms Pellets
Generic Material PVC, Rigid
Generic Name Polyvinyl Chloride, Rigid (PVC, Rigid)
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Construction Applications
General Purpose
Outdoor Applications