LATI Latamid 66 H2PX-V2 PA 66, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2PX-V2 PA 66, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Linear Mold Shrinkage, Flow 0.0115 - 0.0145 cm/cm
0.0115 - 0.0145 in/in
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
55.0 MPa

@Temperature 23.0 °C
 7980 psi

@Temperature 73.4 °F
Elongation at Break 15 %

@Temperature 23.0 °C
 15 %

@Temperature 73.4 °F
80 %

@Temperature 60.0 °C
 80 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 0.500 GPa

@Temperature 120 °C
 72.5 ksi

@Temperature 248 °F
0.700 GPa

@Temperature 90.0 °C
 102 ksi

@Temperature 194 °F
1.25 GPa

@Temperature 60.0 °C
 181 ksi

@Temperature 140 °F
2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
3.50 GPa

@Temperature 150 °C
 508 ksi

@Temperature 302 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 95.0 °C
203 °F
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Vicat Softening Point 195 °C

@Load 5.00 kg
 383 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 30 %
30 %
Glow Wire Test 850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWIT
850 °C

@Thickness 2.00 mm
 1560 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 300 V
300 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa