Ineos ABS Lustran® 266 ABS, Transparent Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 266 ABS, Transparent Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 266 resin is a clear injection molding grade of ABS (acrylonitrile butadiene styrene). This transparent, general-purpose grade provides clarity and toughness with ease of processing. The resin is available in transparent tint, color code 000000. A tough, transparent grade of ABS, Lustran® ABS 266 resin is used in housings, toys, lawn and garden applications, and various consumer goods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM-D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM-D955 |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM-D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM-D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM-D638 |
| Elongation at Break | >= 48 % | >= 48 % | ASTM-D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM-D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM-D638 |
| Flexural Yield Strength | 59.0 MPa | 8560 psi | ASTM-D790 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 3.20 mm |
3.30 ft-lb/in @Thickness 0.126 in |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 121 µm/m-°C | 67.2 µin/in-°F | ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
Unannealed; ASTM-D648 |
| 94.0 °C @Thickness 12.7 mm |
201 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C @Thickness 3.20 mm |
163 °F @Thickness 0.126 in |
Unannealed; ASTM-D648 |
| 82.0 °C @Thickness 12.7 mm |
180 °F @Thickness 0.500 in |
Unannealed; ASTM-D648 | |
| UL RTI, Electrical | 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL746B |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Clear Color |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Clear Color |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.52 | 1.52 | ASTM-D542 |
| Haze | 3.0 % @Thickness 2.54 mm |
3.0 % @Thickness 0.100 in |
ASTM-D1003 |
| Transmission, Visible | 86 % @Thickness 2.54 mm |
86 % @Thickness 0.100 in |
ASTM-D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 195 - 220 °C | 383 - 428 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 225 °C | 392 - 437 °F | Injection Molding |
| Front Barrel Temperature | 205 - 230 °C | 401 - 446 °F | Injection Molding |
| Nozzle Temperature | 205 - 230 °C | 401 - 446 °F | Injection Molding |
| Melt Temperature | 205 - 230 °C | 401 - 446 °F | Injection Molding |
| Mold Temperature | 45.0 - 65.0 °C | 113 - 149 °F | Injection Molding |
| Drying Temperature | 71.0 - 77.0 °C @Time 14400 sec |
160 - 171 °F @Time 4.00 hour |
|
| 82.0 - 88.0 °C @Time 7200 sec |
180 - 190 °F @Time 2.00 hour |
||
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Injection Pressure | 68.9 - 110 MPa | 10000 - 16000 psi | Injection Molding |
| Back Pressure | 0.000 - 0.172 MPa | 0.000 - 25.0 psi | Injection Molding |
| Clamp Pressure | 30.8 - 61.6 MPa | 4470 - 8930 psi | Injection Molding |
| Cushion | <= 0.635 cm | <= 0.250 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hold Pressure | 50-75% of Injection Pressure, Injection Molding | |
| Injection Speed | High | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.75 | Injection Molding |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Santoprene® 451-87 Thermoplastic Rubber (discontinued **)
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 8 PHR Di-Cup 40C
- IRPC Polimaxx Polene G2865 High Density Polyethylene
- Indium Corp. Indalloy® 183 Au-Ge Solder Alloy
- Saint-Gobain CHR® 2042-5 Skived PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Sinvicomp SFE 3500 Polyvinyl Chloride, Flexible
- Zell-Metall Engineering Plastics Zellamid 1500T (PEEK modified)
- DSM Arnitel® PL381-H TPC-ET
- Beijing Ranger Chem PBT-201-G25 202 Environmental Protection Flame Retarding FR PBT
- EG72D Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved