PolyOne Geon™ Vinyl Rigid Extrusion L0660 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L0660 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 38.5 MPa | 5580 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 73.1 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 3.04 GPa | 441 ksi | ASTM D790 |
| Izod Impact, Notched | 1.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.62 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 2.30 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
4.31 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 35.6 J/cm @Temperature 23.0 °C |
0.0667 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 54.7 J/cm @Temperature 23.0 °C |
0.102 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C | 36.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 3.18 mm |
167 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All Colors |
| V-0 @Thickness 0.711 mm |
V-0 @Thickness 0.0280 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | General Purpose | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13264 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |
Users viewing this material also viewed the following:
- Kolon Kocetal® TC704 Reinforced Grade Acetal Copolymer (Unverified Data**)
- Lehmann & Voss LUVOCOM® 1850/CF/15/TF/10/EM PBT, with carbon fiber, PTFE, easy flowing
- LG Chemical ALPHALAC SH860 HIPS
- MetalTek MTEK 175-C Cast UNS C95400HT Aluminum Bronze
- SABIC Innovative Plastics LNP LUBRICOMP SFL2A PA12
- Teknor Apex Monprene® MP-2740L3-UV Thermoplastic Elastomer
- A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy
- China Tungsten YG16C Cemented Tungsten Carbide for Mining Purposes
- Bhansali Engineering Abstron IM-21 ABS Very High Rigidity Injection Molding Grade
- Quadrant EPP Proteus® White Homopolymer Polypropylene (ASTM Product Data Sheet)
Copyright © lookpolymers.com All Rights Reserved