Special Metals NIMONIC® Alloy 901
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | NIMONIC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals NIMONIC® Alloy 901.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy containing titanium and aluminum for precipitation hardening and molybdenum for solid-solution strengthening. The alloy has high yield strength and creep resistance at temperatures to about 1110°F (600°C). A substantial iron content enables the alloy to combine high strength with good forging characteristics. Used in gas turbines for discs and shafts. Standard product form is round.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.14 g/cc | 0.294 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1030 MPa @Temperature 550 °C |
149000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
| 1200 MPa @Temperature 23.0 °C |
174000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 875 MPa @Strain 0.200 % |
127000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 800 MPa @Strain 0.200 %, Temperature 550 °C |
116000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 15 % | 15 % | Precipitation Hardened |
| 10 % @Temperature 550 °C |
10 % @Temperature 1020 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.5 µm/m-°C @Temperature 20.0 - 100 °C |
7.50 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.431 J/g-°C | 0.103 BTU/lb-°F | |
| Melting Point | 1280 - 1345 °C | 2340 - 2453 °F | |
| Solidus | 1280 °C | 2340 °F | |
| Liquidus | 1345 °C | 2453 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.35 % | <= 0.35 % | |
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 11 - 14 % | 11 - 14 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 33 % | 33 % | As remainder |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 5.0 - 6.5 % | 5.0 - 6.5 % | |
| Nickel, Ni | 40 - 45 % | 40 - 45 % | Including Cobalt |
| Silicon, Si | <= 0.40 % | <= 0.40 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Titanium, Ti | 2.8 - 3.1 % | 2.8 - 3.1 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000112 ohm-cm | 0.000112 ohm-cm | |
| Magnetic Permeability | 1.013 | 1.013 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ OM 6240-1 Thermoplastic Elastomer (TPE)
- LG Chemical SSBR 3626 High Acrylonitrile Polymer
- Saint-Gobain CHR® SGC6-04(R) CHEMLAM Copper Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Tisan TISESTER® 30% Glass Fiber Reinforced and heat Stabilized Polybutylene Terephthalate
- DuPont Performance Polymers Zytel® HTN 92G35DH2 BK083 Polyphthalamide (PPA) (Unverified Data**)
- BASF HDO® 1,6-Hexanediol Molten
- A. Schulman ComAlloy Hiloy® 625 Nylon 6/6, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved