Techmer ES HiFill® PC GF20 20% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PC GF20 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Thickness 3.17 mm |
0.0035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 107 MPa | 15500 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 4.83 GPa | 700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm |
3.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.4 µm/m-°C | 13.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 29.9 kV/mm | 760 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5004UV Polyolefin
- SABIC Innovative Plastics LNP LUBRICOMP CG006 PS (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Thermocomp 5C003
- Hexcel® HexPly® M21 356°F (180°C) Curing Epoxy Matrix
- DuPont Teijin Films Melinex® 306 Polyester Film, 300 Gauge
- Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Dry)
- Aclo Accutech Polypropylene Copolymer CP0436C20L Calcium Reinforced
- Aclo Accutech Polypropylene Copolymer CP0436C30L1 Calcium Reinforced
- Arlon 915-07R##-P1 0.015" (0.381 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved