SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
| 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 | |
| 64.0 MPa | 9280 psi | ASTM D638 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
| 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | ASTM D638 | |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.1 % | 1.1 % | Type I, 5 mm/min; ASTM D638 |
| 1.1 % | 1.1 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| 7.08 GPa | 1030 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 85.0 MPa | 12300 psi | ISO 178 |
| 89.0 MPa | 12900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 96.0 MPa | 13900 psi | ASTM D790 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.32 GPa | 917 ksi | 2 mm/min; ISO 178 |
| 6.34 GPa | 920 ksi | ASTM D790 | |
| 6.48 GPa | 940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.56 J/cm | 2.92 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Kennametal Stellite Stellite® 2012 Cobalt Alloy
- ICO Polymers ICORENEâ„¢ 155-1330 LMDPE Rotational Molding Resin
- Lubrizol Hipscon™ M-530 Static Control Polystyrene
- Zeon Chemicals Sivic® Z740 Polyblend Nitrile Elastomer
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Hercoflex 600 Plasticizer
- Beijing Chemical Industry KAIFA® 301-G15RF PBT Resin
- ExxonMobil Mobil Multi-Vehicle ATF
Copyright © lookpolymers.com All Rights Reserved