| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion 87555 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 53.4 MPa | 7750 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.79 GPa | 405 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 88.5 MPa | 12800 psi | ASTM D790 |
| Flexural Modulus | 2.84 GPa | 412 ksi | ASTM D790 |
| Izod Impact, Notched | 1.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.62 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 5.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
10.7 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| 11.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
20.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 52.0 J/cm @Temperature 23.0 °C |
0.0974 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 173 J/cm @Temperature 23.0 °C |
0.324 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.2 °C @Thickness 3.18 mm |
153 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Features | General Purpose | |
| High Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16453 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FC-2110Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- Chevron Phillips EB6025 HIPS - High Impact Polystyrene (discontinued **)
- Kraton® D1126 P (SIS) Radial Copolymer
- Sibur Discar-SL PC/ABS Compositional Polymer
- A. Schulman POLYBATCH™ ASP-2000 Permanent Antistatic Product
- Clariant Renol TPU1088A Polyurethane Elastomer, Aromatic Polyester
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 700 Gauge
- ConocoPhillips Hydroclear® 220 Multipurpose R&O Oil, AGMA Lubricant No. 5
- Trelleborg Z600 Commercial SBR Rubber
Copyright © lookpolymers.com All Rights Reserved