- Lehmann & Voss LUVOCOM® 1105-7828/GY PEEK, with glass fiber
Lehmann & Voss LUVOCOM® 1105-7828/GY PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-7828/GY PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Superheated steam sterilizable.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 g/cc | 1.78 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 130 MPa | 18900 psi | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |
| Flexural Strength | 190 MPa | 27600 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 260 °C | 500 °F | short term | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | grey |
Users viewing this material also viewed the following:
- Osprey Metals 420 Stainless Steel Powder (Grade 90% - 16)
- Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 7781 E-Glass Reinforced
- Polymer Resources PC-GP4 Polycarbonate, General Purpose, Easy Flow
- MarkeTech Calcium Fluoride:Europium (CaF2:Eu) Scintillator Crystal
- Unipetrol PP MONSTEN® TB 002 Polypropylene Homopolymer
- A. Schulman PP 1452 Polypropylene Medium Impact Polypropylene
- Dow C700-35N Polypropylene Impact Copolymer Resin
- DSM Arnite® A02 307 PET
- MF-5040 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved