Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Petroquimica Triunfo
Trade Name Tritheva®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Tritheva TN 2007 resin is an Ethylene-Vinyl Acetate copolymer (EVA), developed to meet the multi-layer packaging needs where are required high strength, with high toughness, and excellent optical properties. These packages may be produced by coextrusion and/or lamination in combination with many others materials as PVdC, PA, EVOH, etc. This product allows for radiation treatment (crosslinking) and a combination with different materials ensures low water vapor and oxygen transition rates (high barrier). These features are specially important to increase the shelf life of fresh food, and other products. The resin has flexibility at low temperature that enhances applications in frozen food bags, and to provide a low temperature heat seal to itself or many other structure and composition commonly used in flexible packaging applications. The melt properties of this resin allow it to be processed on blow film equipments over a wide range of film thickness and blow-up ratios. This product complies with the requirements of Brazilian and corresponding legislation of Mercosul and it is in conformity with FDA Regulations 21 CFR 177.1350, to contact with foodstuff.Applications: High transparency coextruded packaging. Shrinkable packaging for food stuff, such as: cheese, meat, ham, and frozen goods.Resin Properties: Compressed molded plate. Method ASTM D-1928, procedure C. Film obtained on a 50mm blow film line with barrier screw, 25:1 L/D, 1.0mm die gap, 50µm gauge, 2.3:1 BUR.Information provided by Dax Resinas
Physical Properties Metric English Comments
Density 0.933 g/cc
0.0337 lb/in³
ASTM D1505
Vinyl Acetate Content 9.0 - 11 %
9.0 - 11 %
Thickness 50.0 microns
1.97 mil
Melt Index of Compound 0.50 - 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.50 - 0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.0 MPa
3190 psi
ASTM D638
Tensile Strength, Yield 6.00 MPa
870 psi
ASTM D638
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 730 %
730 %
ASTM D882
Elongation at Break 720 %
720 %
ASTM D638
Secant Modulus, MD 0.0620 GPa
8.99 ksi
5%; ASTM D882
Secant Modulus, TD 0.0610 GPa
8.85 ksi
5%; ASTM D882
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ASTM D882
Film Tensile Strength at Break, TD 25.0 MPa
3630 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 99.0 °C
210 °F
ASTM D3418
Optical Properties Metric English Comments
Haze 2.3 %
2.3 %
ASTM D1003
Gloss 82 %
82 %
45° - Gardner; ASTM D2457
130 %
130 %
@ 60° Gardner; ASTM D2457
Processing Properties Metric English Comments
Processing Temperature 140 - 155 °C
284 - 311 °F
Plasticizing Zone
155 - 170 °C
311 - 338 °F
Mixture Zone
Feed Temperature 140 - 150 °C
284 - 302 °F
Adapter Temperature 170 - 190 °C
338 - 374 °F
Blow-up Ratio (BUR) 3.0
3.0
Recommended