- PolyOne Edgetek® UR-20CF/000 Thermoplastic Elastomer - TPU, Carbon Fiber Reinforced (discontinued **)
PolyOne Edgetek® UR-20CF/000 Thermoplastic Elastomer - TPU, Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® UR-20CF/000 Thermoplastic Elastomer - TPU, Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0035 cm/cm | 0.0030 - 0.0035 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 55.2 MPa | 8000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 3.45 GPa | 500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
16.0 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1000 ohm-cm - 1e+05 | 1000 ohm-cm - 1e+05 | ASTM D257 |
| Surface Resistivity per Square | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 216 - 238 °C | 420 - 460 °F | Molding |
| Mold Temperature | 15.6 - 37.8 °C | 60.0 - 100 °F | |
| Drying Temperature | 93.3 - 110 °C | 200 - 230 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6010 Adhesive
- SABIC Innovative Plastics LNP FARADEX AS002 ABS (Asia Pacific)
- SABIC Innovative Plastics LNP Lubricomp WBG16 PBT (Europe-Africa-Middle East)
- Saint-Gobain Rulon® LR Grade Bearing/Seal PTFE
- Teknor Apex Monprene® MP-2750L1 Thermoplastic Elastomer
- A. Schulman POLYFORT™ PP 3719 Impact Copolymer Polypropylene
- Aclo Accutech Polypropylene Homopolymer HP0339G10CL Glass Reinforced Coupled
- BASF Paliotol™ Yellow K 2270 Color Additive
- ACC EP RAP 60 EPI Engineered Polymers Aliphatic Polyurea
- 3M Scotch-Weld™ SI40 Surface Insensitive Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved