PolyOne Edgetek® PF-40GF/000 Polysulfone, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PF-40GF/000 Polysulfone, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Water Absorption | 0.18 % | 0.18 % | 24 hr. Immersion; ASTM D570 |
| Water Absorption at Saturation | 0.58 % | 0.58 % | Long-Term Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 92 | 92 | ASTM D785 |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 183 MPa | 26600 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 176 MPa | 25500 psi | ASTM D695 |
| Shear Strength | 68.9 MPa | 10000 psi | ASTM D732 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C |
12.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.360 W/m-K | >= 2.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 380 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | Annealed, 0.125 in bars; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All Colors; 0.062 in.; PolyOne Internal |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 360 - 382 °C | 680 - 720 °F | Molding |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- LyondellBasell Ethanol, 200 Proof
- LG Chemical Lupoy 3030-15 Polycarbonate Resin
- Lucent Polymers PC-1428FD Polycarbonate, FDA Compliant, Injection Grade
- Lanxess Pocan® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber
- Taiwan PU Corporation CPU-69-A/B Mixing Ratio 100/40 Polyurethane Casting Elastomer
- Solvay TECHNYL® eXten D 437P PA6.10
- Teijin Panlite® LV-2225L Standard (mold release/ice color grade) Polycarbonate Resin
- SABIC Innovative Plastics XYLEX EXXX0292 PC+POLYESTER (Europe-Africa-Middle East)
- Lubrizol Estane® 2102-65D Thermoplastic Polyurethane Elastomer
- DSM Arnitel® PL581 Polyether Ester Elastomer (European and Asian Grade)
Copyright © lookpolymers.com All Rights Reserved