Overview of materials for Thermoset Polyurethane, Elastomer, Glass Filled

Category Polymer , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Glass Filled , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Thermoset Polyurethane, Elastomer, Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.950 - 1.25 g/cc
0.0343 - 0.0452 lb/in³
Average value: 1.16 g/cc Grade Count:11
Water Absorption at Saturation 0.100 - 2.80 %
0.100 - 2.80 %
Average value: 1.16 % Grade Count:5
Linear Mold Shrinkage 0.00430 - 0.00750 cm/cm
0.00430 - 0.00750 in/in
Average value: 0.00607 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 16.0 - 38.0 MPa
2320 - 5510 psi
Average value: 27.4 MPa Grade Count:11
Elongation at Break 15.0 - 200 %
15.0 - 200 %
Average value: 86.5 % Grade Count:11
Flexural Modulus 0.470 - 2.07 GPa
68.2 - 300 ksi
Average value: 1.20 GPa Grade Count:11
Izod Impact, Notched 0.500 - 4.30 J/cm
0.937 - 8.06 ft-lb/in
Average value: 1.82 J/cm Grade Count:9
Tear Strength 70.0 - 140 kN/m
399 - 799 pli
Average value: 107 kN/m Grade Count:11
Thermal Properties Metric English Comments
CTE, linear 49.0 - 137 µm/m-°C
27.2 - 76.1 µin/in-°F
Average value: 75.3 µm/m-°C Grade Count:10