PolyOne Edgetek® NY-20CF/000 BLACK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NY-20CF/000 BLACK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 193 MPa | 28000 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C @Thickness 1.57 mm |
430 °F @Thickness 0.0618 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C @Thickness 1.57 mm |
421 °F @Thickness 0.0618 in |
Annealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 293 °C | 500 - 559 °F | |
| Mold Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Drying Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Filler / Reinforcement | Carbon Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- MV Labs EU410 EuCl3·6H2O Europium(III) chloride hexahydrate
- Osprey Metals 420/MA Stainless Steel Powder (Grade 95% - 16)
- Nilit FRIANYL B63 V2 Nylon 6.6 for injection molding
- Lehmann & Voss LUVOCOM® 1105-8534 PEEK, with mineral filler
- Intercontinental Polymers HoPET 728-02 HoPET Polymer Type - Clear, Polyester Pellets
- Schott Glass 8689 Borosilicate Glass
- Chosun Refractories B-1 Insulating Firebrick
- Bhansali Engineering Abstron IMC-45 FR V2 Flame Retardant PC/ABS Grade
- Solvay Chemicals Hydrochloric Acid 31% - Technical Grade (20 wt% - 28 wt% Concentration)
Copyright © lookpolymers.com All Rights Reserved