PolyOne Edgetek® AT-25GF/000 Acetal-Copolymer, Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AT-25GF/000 Acetal-Copolymer, Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.586 g/cc | 1.586 g/cc | ASTM D792 |
| Water Absorption | 0.040 % @Thickness 3.17 mm |
0.040 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0055 cm/cm | 0.0050 - 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Unannealed, 0.125 in bars; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | Molding |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD911A PC (Europe-Africa-Middle East)
- Renegade Materials Corporation RM-3006 Bismaleimide (BMI) Paste Adhesive
- Techmer ES HiFill® PA6/6 GF12 TL20 12% Glass Filled
- Suzhou Hipro Polymers Hiprolon® 70 MC HLS G30 Nylon 610, 30% glass fiber filled
- A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene
- Covestro Makrolon® Rx1805 Polycarbonate
- ChevronTexaco Pinnacle® EP 220
- Hippe PF CC 33 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- DuPont Teijin Films Mylar® RSX Polyester Film, 300 Gauge
- ChevronTexaco Ulti-Plex® NLGI 0 Greases EP
Copyright © lookpolymers.com All Rights Reserved