ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Exxon Chemical
Trade Name LLDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 1004YB is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements for insulation. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: Halogen-free flame retardant (HFFR) compoundsLV silane cross-linkable insulation – 1 step processLV silane cross-linkable insulation – 2-step processInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 2.8 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.8 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 48

@Time 15.0 sec
48

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 13.1 MPa
1900 psi
ASTM D638
Tensile Strength, Yield 11.7 MPa
1700 psi
ASTM D638
Elongation at Break 710 %
710 %
ASTM D638
Elongation at Yield 20 %
20 %
ASTM D638
Flexural Modulus, 1% Secant 248 MPa
36000 psi
ASTM D790
Thermal Properties Metric English Comments
Melting Point <= 250 °C
<= 482 °F
Peak Melting Point; ExxonMobil method
Electrical Properties Metric English Comments
Volume Resistivity 4.80e+15 ohm-cm
4.80e+15 ohm-cm
ASTM D257
Dielectric Constant 2.2

@Frequency 60.0 Hz
2.2

@Frequency 60.0 Hz
ASMT D150
Dielectric Strength 51.2 kV/mm
1300 kV/in
ASTM D149
Dissipation Factor 0.00040

@Frequency 60.0 Hz
0.00040

@Frequency 60.0 Hz
ASMT D150