- PolyOne Edgetek® AS-30GF/000 FRVO Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
PolyOne Edgetek® AS-30GF/000 FRVO Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AS-30GF/000 FRVO Acrylonitrile Butadiene Styrene (ABS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedFlame RetardantUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 75.8 MPa | 11000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 68.9 MPa | 10000 psi | ASTM D695 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 28.8 µm/m-°C @Temperature 20.0 °C |
16.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.231 W/m-K | >= 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 227 - 277 °C | 440 - 530 °F | Molding |
| Mold Temperature | 60.0 - 93.3 °C | 140 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- PPT BP860 NiZn Ferrite Powder
- Northstar Polymers MPP-D65A Polyether Base Polyurethane Resin
- NOVA Chemicals Novapol® HE-D250A HDPE Extrusion Resin (discontinued **)
- Lanxess Pocan® B 1100 000000 PBT
- Sylvin Technologies 9600-70 Clear PVC Molding Compound
- Solvay Specialty Polymers Amodel® A-1625 HS Polyphthalamide (PPA), 25% GlassCarbon Fiber
- SABIC Innovative Plastics LNP STAT-KON DX91077 PC
- Bostik 1525 Medium Performance, Oil Resistant Polyamide Glue Stick
- Polystrand ThermoPro™ IE7015X X-Ply Cross-Ply Polypropylene-Glass Composite
- Fainplast Compounds GA 86/R Flexible PVC, Flame Retardant Sheathing
Copyright © lookpolymers.com All Rights Reserved