- Malvern Minerals Sliastic 437 with 50% Novacite® L-207A Quartz Filler
Malvern Minerals Sliastic 437 with 50% Novacite® L-207A Quartz Filler
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Malvern Minerals Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Malvern Minerals Sliastic 437 with 50% Novacite® L-207A Quartz Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Press Vulcanized 5 minutes at 260° F. Product data demonstrates the effect of the Novacite® filler.Information provided by Malvern Minerals Company.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 53 | 53 | Oven cured 4 hours at 480°F |
| 58 | 58 | Heat Aged 24 hours at 600F | |
| Tensile Strength at Break | 4.07 MPa | 590 psi | Heat Aged 24 hours at 600F |
| 6.27 MPa | 910 psi | Oven cured 4 hours at 480°F | |
| Elongation at Break | 200 % | 200 % | Heat Aged 24 hours at 600F |
| 340 % | 340 % | Oven cured 4 hours at 480°F | |
| Tear Strength | 11.4 kN/m | 65.0 pli | Die B |
| Compression Set | 26 % @Temperature 177 °C, Time 79200 sec |
26 % @Temperature 350 °F, Time 22.0 hour |
Oven cured 4 hours at 480°F |
Users viewing this material also viewed the following:
- MV Labs ER300 Er2(CO3)3·xH2O Erbium carbonate hydrate
- SABIC Innovative Plastics ULTEM 1010R PEI (Asia Pacific)
- Techmer ES HiFill® ABS GF20 20% Glass Filled
- Wingate Alloys Champaloy Clad Overlay Wear Plate, Chrome Carbide Fusion Plate
- Eastman Tenite 285A3R30018 Butyrate Natural, Trsp
- Braskem Idealis 500 High Molecular Weight Polyethylene Powder
- ExxonMobil OPPalyte® 310 HSTW OPP Film
- Lucobit Lucobit® 1235 Ethylene Copolymer Bitumen
Copyright © lookpolymers.com All Rights Reserved