PolyOne Bergamid™ A70 G35 UF SO Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ A70 G35 UF SO Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc @Temperature 23.0 °C |
0.0531 lb/in³ @Temperature 73.4 °F |
±0.03 g/cm³; DIN 53479 |
| Ash | >= 35 % | >= 35 % | ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
18900 psi @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2/5 |
| Elongation at Break | 2.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
2.0 % @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2/5 |
| Tensile Modulus | 12.0 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
1740 ksi @Thickness 0.157 in, Temperature 73.4 °F |
ISO 527-2/1 |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.750 J/cm² @Temperature 23.0 °C |
3.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 261 °C | 502 °F | ISO 3146 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous (GTP 50% Tensile); IEC 60216 |
| 220 °C | 428 °F | Short Time; IEC 60216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
ALL; UL 94 |
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 | |
| Glow Wire Test | 960 °C @Thickness 0.800 - 3.00 mm |
1760 °F @Thickness 0.0315 - 0.118 in |
0.8 mm wire; Ignition Temperature; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Flame Retardant | |
| Halogen Free | ||
| Low (to None) Phosphorus Content | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 35% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Kraton® D1102 + LDPE blend (6/94)
- Silberline Silvet® 420-30-E1
- Saint-Gobain Vitreosil® CFQ/TSC Optical Fused Quartz
- SCG Chemicals EL-Leneâ„¢ M40 Butene (C4) Rotational Molding Resin
- Teknor Apex Sinpolene MBB1232 Linear Low Density Polyethylene
- Eagle Brass 425 Tin Brass 2%, 3/4 Hard
- Ecomass® 1080ZD94 Tungsten Filled Polyamide
- ALM FR 106 Nylon 11 SLS Prototyping Polymer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Black Peroxide Cure
- Lucite International Diakon® Frost 902 80 Acrylic Polymer
Copyright © lookpolymers.com All Rights Reserved