BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 Q611 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.6 % | 6.6 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 130 cm³/g | 130 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 275 °C |
25 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 65.0 MPa | 9430 psi | 5mm/min; ISO 527 |
| Elongation at Break | 12 % | 12 % | 5mm/min; ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | 1mm/min; ISO 527 |
| Tensile Creep Modulus, 1 hour | 2800 MPa | 406000 psi | ISO 899 |
| Tensile Creep Modulus, 1000 hours | 1850 MPa | 268000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz |
6.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Outokumpu 4841 High Temperature Austenitic Stainless Steel
- SABIC Innovative Plastics Cycoloy® MC8200 PC+ABS (Asia Pacific)
- Solvay Engineered Polymers INDURE™ E1500 HG TPO (discontinued **)
- Indium Corp. Sn992 Pb-Free Soldering Alloy
- Isoflon PTFE +28% GL Blue-E glass-1% Blue Polytetrafluoroethylene with 28% GL-Blue-E glass-1% Blue (equivalent VX1)
- Shandong Dongyue Polymer DF-204 PTFE Fine Powder
- Special Metals INCONEL® C276 Nickel Superalloy Tubing, 30% Cold Work
- Covestro Bayflex® MP-10000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- SABIC Innovative Plastics Lexan® 943 PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved