Polimeri Europa SINKRAL L320/G ABS, Platable Grade (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa SINKRAL L320/G ABS, Platable Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-25-16-20 Injection moulding grade, tailored for electroplating. It is a high flow grade with a good impact resistance. Applications: Items , even of complex shapes, with high aesthetic aspect for the following sectors: appliances: window frames of washing machines automotive: grilles, car emblems cosmetic: tops. Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains lubricant and release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Water Absorption	1.0 %	1.0 %
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Humidity Absorption
Melt Flow	30 g/10 min @Load 10.0 kg, Temperature 220 °C	30 g/10 min @Load 22.0 lb, Temperature 428 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	43.0 MPa	6240 psi	50 mm/min
Elongation at Break	10 %	10 %	Nominal
Elongation at Yield	3.2 %	3.2 %	50 mm/min
Tensile Modulus	2.30 GPa	334 ksi	1 mm/min
Charpy Impact Unnotched	17.0 J/cm²	80.9 ft-lb/in²
	11.0 J/cm² @Temperature -30.0 °C	52.4 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	1.80 J/cm²	8.57 ft-lb/in²
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	90.0 µm/m-°C @Temperature 20.0 °C	50.0 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F
Vicat Softening Point	97.0 °C	207 °F	50°C/hr; 50N
Glass Transition Temp, Tg	105 °C	221 °F	10°C/min test
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Strength	30.0 kV/mm	762 kV/in
Comparative Tracking Index	600 V	600 V