Polimeri Europa EDISTIR N1461 Polystyrene (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR N1461 Polystyrene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,M,085-03 High molecular weight general purpose polystyrene with good mechanical strength. Well suitable for injection molding of complex items which require good toughness and improved elasticity. Applications: Typical injection molding application is the CD box.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | 5 mm/min |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min |
| Tensile Modulus | 3.25 GPa | 471 ksi | 1 mm/min |
| Charpy Impact Unnotched | 1.50 J/cm² | 7.14 ft-lb/in² | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | |
| Vicat Softening Point | 90.0 °C | 194 °F | 50°C/hr; 50N |
| Glass Transition Temp, Tg | 89.0 °C | 192 °F | 10°C/min test |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Manufacturer specifies 'transparent' but doesn't quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 70.0 kV/mm | 1780 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| Comparative Tracking Index | 400 V | 400 V |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 925A PC (Europe-Africa-Middle East)
- Quadrant EPP Semitron® ESd 225 POM-C, static dissipative, extruded (ISO Data)
- LATI Laticonther 87/28 GR/50 PC, 50% Graphite Reinforced
- SABIC Innovative Plastics NORYL V01525 PPE+HIPS (Asia Pacific)
- Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR
- ExxonMobil Santoprene® 271-87 Thermoplastic Elastomer
- CIMBAR CIMBAR™ BF Barite Powder (BaSO4)
- Braskem LL3800N HDPE Cast Film Extrusion Polyethylene Copolymer
- Beijing Chemical Industry KAIFA® 301-G10F PBT Resin
- Chevron Phillips Ryton® R-4 04 PPS (Polyphenylene Sulfide) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved