ExxonMobil Oppalyte™ 60MH247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 60MH247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, modified higher density, biaxially oriented PP film. This opaque and stiff film is ideal for mono material requirements and it has been designed for cold seal applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent stiffness and flex resistanceOutstanding opacity, white background and reduced show-throughGood moisture barrierExceptional printability and receptivity to coatingsExcellent support for cold seal adhesionFeatures: Light BarrierApplications:Bakery Biscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen Food Household and Detergents Uses: HFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Transmission Rate | 0.636 cc/m²/day @Temperature 23.0 °C |
0.0410 cc/100 in²/day @Temperature 73.4 °F |
Wet, 75% RH; ExxonMobil Method |
| 2.48 cc/m²/day @Temperature 23.0 °C |
0.160 cc/100 in²/day @Temperature 73.4 °F |
0% RH; ExxonMobil Method | |
| Thickness | 61.0 microns | 2.40 mil | ExxonMobil Method |
| Coating Weight | 42.9 g/m² | 26.8 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 170 % | 170 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 105 MPa | 15200 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 20 % | 20 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 16100 in2/lb |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 2318 LLDPE Injection Molding Resin (discontinued **)
- Loxim 830 02C HB Polypropylene Compound, 30% Calcite Filled, Flame Retardant
- Karina E 5525/1-TRE Kariprene Natural.
- A. Schulman POLYFORT™ FPP 1245U CaCO3 Filled UV Stable Copolymer Polypropylene
- ExxonMobil ESCOREZ™ 1315 Petroleum Hydrocarbon Resin
- Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing
- Barlog Plastics KEBAFLEX SG 85 A.1 TPE-S, Shore A85, natural
- Polymer Resources PPX-MF-FR1 Modified PPO, UL 94 V-0 with HDT of 190 F, Mineral Reinforced (Unverified Da
Copyright © lookpolymers.com All Rights Reserved