Polikim KESTAMID® PA6G Polyamide 6

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Polikim Polimer ve Kimya Sanay
Trade Name KESTAMID®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polikim KESTAMID® PA6G Polyamide 6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kestamid® is also known as Cast Polyamide or Cast Nylon. Kestamid® is an engineering plastic used commonly in all industrial branches for its superior mechanical, physical, chemical and electrical properties. It is replacing aluminum, copper, bronze, steel, fiber, brass and other metals in many applications with superior advantages. It is cheaper, lighter, harder and more durable than these metals. In terms of cost, Kestamid® is 1/7th of bronze, 1/5th of copper and 1/3rd of brass. As its density is low, purchase and delivery costs become less. Using Kestamid® instead of metal components helps push selling price and delivery cost down. It contributes significantly to the final producer in reducing costs and increasing market share. As it does not require lubrication, maintenance costs are also reduced to a minimum. High wear and impact resistances make Kestamid® durable. Taking its operational life into consideration, the advantages and superiorities of Kestamid® compared to the above-mentioned metals become even more obvious. Kestamid® is a “fix and forget” type of material. It is possible to produce steel bush core gears, pulleys and mixer fans or produce cylinders with steel axis by making use of techniques specific to the production of Kestamid® combined with the mechanical resistance of metals.Information provided by Polikim Polimer.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Water Absorption at Saturation 7.0 %
7.0 %
ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 84
84
ISO 868
Tensile Strength, Ultimate 83.4 MPa
12100 psi
ISO 527
Elongation at Break >= 20 %
>= 20 %
ISO 527
Tensile Modulus 4.00 GPa
580 ksi
ISO 527
Compressive Strength 93.2 MPa
13500 psi
ISO 604
Compressive Modulus 2.70 GPa
392 ksi
ISO 604
Izod Impact, Notched (ISO) 5.60 kJ/m²
2.66 ft-lb/in²
ISO 180
Charpy Impact Unnotched NB
NB
ISO 179
Coefficient of Friction 0.39
0.39
K Factor (Wear Factor) 0.44
0.44
[mg/km]
K (wear) Factor 500 x 10-8 mm³/N-M
248 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
CTE, linear 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359
Melting Point 220 °C
428 °F
Maximum Service Temperature, Air 110 °C
230 °F
continuous
170 °C
338 °F
short term
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ISO 60093
Surface Resistance >= 1.00e+13 ohm
>= 1.00e+13 ohm
ISO 60093
Dielectric Constant 3.7
3.7
ISO 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
ISO 50243