PlastiComp Complet® LGF20 - PP Homopolymer Polypropylene, 20% Long Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler
Manufacturer	PlastiComp
Trade Name	Complēt®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PlastiComp Complet® LGF20 - PP Homopolymer Polypropylene, 20% Long Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 20% long glass fiber reinforcementInformation provided by PlastiComp, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D-792
Filler Content	20 %	20 %	Long Glass Fiber

Mechanical Properties	Metric	English	Comments
Tensile Strength	100 MPa	14500 psi	ASTM D-638
Elongation at Break	3.0 - 4.0 %	3.0 - 4.0 %	ASTM D-638
Tensile Modulus	4.345 GPa	630.2 ksi	ASTM D-638
Flexural Strength	145 MPa	21000 psi	ASTM D-790
Flexural Modulus	4.345 GPa	630.2 ksi	ASTM D-790
Izod Impact, Notched	2.14 J/cm	4.01 ft-lb/in	ASTM D-256
Izod Impact, Unnotched	6.942 J/cm	13.01 ft-lb/in	ASTM D-4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	146 °C	295 °F	ASTM D-648

Processing Properties	Metric	English
Rear Barrel Temperature	199 - 210 °C	390 - 410 °F
Middle Barrel Temperature	204 - 216 °C	400 - 420 °F
Front Barrel Temperature	210 - 221 °C	410 - 430 °F
Nozzle Temperature	204 - 216 °C	400 - 420 °F
Melt Temperature	210 - 221 °C	410 - 430 °F
Mold Temperature	79.4 °C	175 °F
Injection Velocity	50.8 - 76.2 mm/sec	2.00 - 3.00 in/sec
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.635 cm	0.250 in
Screw Speed	30 - 50 rpm	30 - 50 rpm

Descriptive Properties	Value	Comments
Injection Pressure	Medium to maximum