- Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler
Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | PLASTALEN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom PLASTALEN® PC 69 T 10 003/1M Polypropylene reinforced with mineral filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified PP copolymer for injection molding with the content of 10% mineral filler. Application in all automotive industry. Delivered in black.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 10 % | 10 % | |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | STN EN ISO 294-4 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 MPa | 2900 psi | STN EN ISO 527-2 |
| Elongation at Break | 4.0 % | 4.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 1.55 GPa | 225 ksi | STN EN ISO 527-2 |
| Flexural Strength | 25.0 MPa | 3630 psi | STN EN ISO 178 |
| Flexural Modulus | 1.15 GPa | 167 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
STN EN ISO 179 |
| NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 135 °C | 275 °F | STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Noble Polymers Ecobarrier™ 0414 Thermoplastic Olefin (TPO)
- Northstar Polymers SBA-041 Polyester Curing Agent
- Lehmann & Voss LUVOCOM® 1301-7953 PPS, linear, with carbon fiber and PTFE
- H.C. Starck Baymetec® Niobium Ethoxide
- Chicago Extruded Metals BioBrass® UNS C27450 Copper-Zinc Alloy
- Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, Conditioned
- Arlon R33826R017 0.017" (0.432mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ TF 2053Z PTFE Fine Powder
- Arlon R38726R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Fainplast Compounds MGS 86 Medical Flexible PVC, Injection Molding
Copyright © lookpolymers.com All Rights Reserved