PTS Trimid® N6-M200HL Impact Modified Heat Stabilized Nylon 6 with Lube

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Trimid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Trimid® N6-M200HL Impact Modified Heat Stabilized Nylon 6 with Lube.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 37.9 MPa
5500 psi
ASTM D638
Tensile Strength, Yield 55.8 MPa
8090 psi
ASTM D638
Elongation at Break 80 %
80 %
ASTM D638
Flexural Yield Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 2.07 GPa
300 ksi
ASTM D790
Izod Impact, Notched 1.28 J/cm

@Thickness 3.17 mm
 2.40 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 216 °C
421 °F
ASTM D789
Processing Properties Metric English Comments
Rear Barrel Temperature 138 - 216 °C
280 - 420 °F
Middle Barrel Temperature 227 - 254 °C
440 - 490 °F
Front Barrel Temperature 238 - 266 °C
460 - 510 °F
Nozzle Temperature 238 - 266 °C
460 - 510 °F
Melt Temperature 232 - 271 °C
450 - 520 °F
Mold Temperature 21.1 - 93.3 °C
70.0 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 3 - 4 hour
3 - 4 hour
Injection Pressure 82.7 - 172 MPa
12000 - 25000 psi
Back Pressure 0.000 - 0.345 MPa
0.000 - 50.0 psi
Screw Speed 40 - 80 rpm
40 - 80 rpm