Ascend Performance Materials Vydyne® ECO-315 Nylon 66/6, non-halogenated, ignition resistant, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® ECO-315 Nylon 66/6, non-halogenated, ignition resistant, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® ECO315 is non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth AmericaAdditive:Flame RetardantLubricantFeatures:DuctileGood Mold ReleaseHalogen FreeIgnition ResistantLow DensityLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	ISO 1183
Water Absorption	0.80 %	0.80 %	24 hrs; ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage	0.012 cm/cm @Thickness 2.00 mm	0.012 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.014 cm/cm @Thickness 2.00 mm	0.014 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	52.0 MPa	7540 psi	ISO 527-2
Elongation at Break	30 %	30 %	ISO 527-2
Elongation at Yield	20 %	20 %	ISO 527-2
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-2
Flexural Strength	45.0 MPa	6530 psi	ISO 178
Flexural Modulus	1.56 GPa	226 ksi	ISO 178