Special Metals INCOLOY® Alloy 925
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy 925.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A precipitation-hardenable nickel-iron-chromium alloy with additions of molybdenum and copper. It combines the high strength of a precipitation-hardenable alloy with the excellent corrosion resistance of INCOLOY alloy 825. The alloy has outstanding resistance to general corrosion, pitting, crevice corrosion, and stress-corrosion cracking in many aqueous environments including those containing sulfides and chlorides. Used for surface and down-hole hardware in sour gas wells and for oil-production equipment. Standard product forms are round, flats, forging stock, pipe, tube, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.05 g/cc | 0.291 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 970 MPa @Temperature 550 °C |
141000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
| 1210 MPa @Temperature 23.0 °C |
175000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 810 MPa @Strain 0.200 % |
117000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 700 MPa @Strain 0.200 %, Temperature 550 °C |
102000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 24 % | 24 % | Precipitation Hardened |
| 25 % @Temperature 550 °C |
25 % @Temperature 1020 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 100 °C |
7.33 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| Melting Point | 1311 - 1366 °C | 2392 - 2491 °F | |
| Solidus | 1311 °C | 2392 °F | |
| Liquidus | 1366 °C | 2491 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.30 % | 0.30 % | |
| Carbon, C | 0.010 % | 0.010 % | |
| Chromium, Cr | 21 % | 21 % | |
| Copper, Cu | 1.8 % | 1.8 % | |
| Iron, Fe | 28 % | 28 % | |
| Molybdenum, Mo | 3.0 % | 3.0 % | |
| Nickel, Ni | 44 % | 44 % | |
| Titanium, Ti | 2.1 % | 2.1 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000117 ohm-cm | 0.000117 ohm-cm | |
| Magnetic Permeability | 1.001 | 1.001 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9735C TPE, ABS/PC Overmold
- SABIC Innovative Plastics Cycoloy® MC5220 PC+ABS (Asia Pacific)
- M. Holland Company GS411 Polystyrene (discontinued **)
- LNP Stat-Kon® EC-1004 Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Intercontinental Polymers 555 PBT Polymer Elastomer Polyester Pellets
- Lubriplate FMO-85-AW Spray Food Grade Spray Lubricant
- Borealis LE0516 Polyethylene Compound, Crosslinkable, Semiconductive
- Aleris Weldural Aluminum Alloy, 500 mm Thickness
- ExxonMobil Mobil Almo 532
- Michelman® StaticBan® 1005N Heat resistant conductive coating
Copyright © lookpolymers.com All Rights Reserved