PTS BLACK PPE/Nylon Alloy 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS BLACK PPE/Nylon Alloy 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PTS LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 138 MPa | 20000 psi | ASTM D638 |
| Elongation at Break | 7.5 % | 7.5 % | ASTM D638 |
| Flexural Strength | 228 MPa | 33100 psi | ASTM D792 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D792 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 3.17 mm |
1.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 246.1 °C | 475.0 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF20 - PA6 Nylon 6, 20% Long Glass Fiber Reinforced
- Polymer Resources PCSF-FR Polycarbonate, 5% Glass Reinforced Structural Foam Grade
- Mateck LiGaO2
- Fiberfil® J-60/20/E8/M Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- SPS Guang Zhou SAMATâ„¢ 5003 Flame-retarded Polypropylene
- Struktol TPW 113 Processing Additive
- ExxonMobil HDPE HD 6706.62 High Density Polyethylene Copolymer Resin
- Asahi Kasei Thermylene® P-40TC-8100 Chemically Coupled Polypropylene Compound, 40% Talc Filled
Copyright © lookpolymers.com All Rights Reserved