Solvay Specialty Polymers Radel® R-5100 Polyphenylsulfone (PPSU), Filled
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polyphenylsulfone, Glass or Carbon Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Radel® R-5100 Polyphenylsulfone (PPSU), Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Radel® R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, that offers exceptional hydrolytic stability, and toughness superior to other commercially-available, high-temperature engineering resins. This resin also offers a high deflection temperature and outstanding resistance to environmental stress cracking. Radel® polymers are inherently flame retardant, provide excellent thermal stability and possess good electrical properties.Features: Acid Resistant; Autoclave Sterilizable; Base Resistant; Biocompatible; E-beam Sterilizable; Ethylene Oxide Sterilizable; Flame Retardant; General Purpose; Good Chemical Resistance; Good Sterilizability; Good Thermal Stability; Heat Sterilizable; High ESCR (Stress Crack Resist.); High Heat Resistance; Hydrolytically Stable; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam Sterilizable; Ultra High ToughnessUses: Aerospace Applications; Aircraft Applications; Connectors; Dental Applications; Food Service Applications; Hospital Goods; Medical Devices; Medical/Healthcare Applications; Plumbing Parts; Surgical InstrumentsAutomotive Specifications ASTM D6394 SP0312Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.37 % @Time 86400 sec |
0.37 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.6 MPa | 10100 psi | ASTM D638 |
| Tensile Strength, Yield | 69.6 MPa | 10100 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Elongation at Yield | 7.2 % | 7.2 % | ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | ASTM D638 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Compressive Strength | 98.9 MPa | 14300 psi | ASTM D695 |
| Compressive Modulus | 1.73 GPa | 251 ksi | ASTM D695 |
| Poissons Ratio | 0.42 | 0.42 | ASTM E132 |
| Shear Strength | 62.7 MPa | 9090 psi | ASTM D732 |
| Izod Impact, Notched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Tensile Impact Strength | 399 kJ/m² | 190 ft-lb/in² | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 56.0 µm/m-°C | 31.1 µin/in-°F | |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 220 °C | 428 °F | ASTM E1356 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| Oxygen Index | 38 % | 38 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.672 | 1.672 | ASTM D542 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+15 ohm-cm | 9.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.44 @Frequency 60.0 Hz |
3.44 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | ASTM D149 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| NSF | Yes | Yes | NSF 51; NSF 61 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 321 °C | 610 °F | |
| Middle Barrel Temperature | 349 °C | 660 °F | |
| Front Barrel Temperature | 349 °C | 660 °F | |
| Melt Temperature | 343 - 388 °C | 649 - 730 °F | |
| Mold Temperature | 138 - 163 °C | 280 - 325 °F | |
| Drying Temperature | 149 °C @Time 9000 sec |
300 °F @Time 2.50 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | FAA FAR 25.853a; ISO 10993 | |
| Availability | Asia Pacific | |
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Colors; Light Beige; Opaque | |
| Form | Pellets | |
| Processing Technique | Blow Molding; Extrusion; Film Extrusion | |
| Injection Molding; Machining | ||
| Profile Extrusion; Sheet Extrusion; Thermoforming | ||
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.2:1.0 |
Users viewing this material also viewed the following:
- Fiberfil® FPI-15 BK Nylon 6, 15% Glass Reinforced, post industrial
- Styrolution PS 147F GPPS
- SABIC Innovative Plastics Noryl GFN2L PPE+HIPS (Asia Pacific)
- Schmolz + Bickenbach UGISTEAD UGI 204Cu Low Nickel Bar
- Plastics Group Polifil® C-20 20% Calcium Carbonate-Reinforced Polypropylene
- DuPont Appeel® LSR20D752 Lidding Sealant Resin
- A. Schulman PP 1500X-01 Polypropylene High Impact Copolymer Polypropylene
- DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 50 Gauge
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 5.0 PHR Wacker HDK N20 Filler
Copyright © lookpolymers.com All Rights Reserved