Overview of materials for Epoxy Molding Compound

Category Polymer , Thermoset , Epoxy , Epoxy Molding Compound
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Epoxy Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.550 - 2.45 g/cc
0.0199 - 0.0885 lb/in³
Average value: 1.76 g/cc Grade Count:71
Apparent Bulk Density 0.700 - 1.30 g/cc
0.0253 - 0.0470 lb/in³
Average value: 0.950 g/cc Grade Count:5
Water Absorption 0.00340 - 0.600 %
0.00340 - 0.600 %
Average value: 0.179 % Grade Count:17
Moisture Absorption at Equilibrium 0.230 - 0.600 %
0.230 - 0.600 %
Average value: 0.363 % Grade Count:12
Viscosity 600 - 45000 cP

@Temperature 165 - 175 °C
600 - 45000 cP

@Temperature 329 - 347 °F
Average value: 6480 cP Grade Count:48
1700 - 1700 cP

@Temperature 175 - 175 °C
1700 - 1700 cP

@Temperature 347 - 347 °F
Average value: 6480 cP Grade Count:1
1700 - 1700 cP

@Diameter 0.500 - 0.500 mm
1700 - 1700 cP

@Diameter 0.0197 - 0.0197 in
Average value: 6480 cP Grade Count:1
Linear Mold Shrinkage 0.000200 - 0.00700 cm/cm
0.000200 - 0.00700 in/in
Average value: 0.00211 cm/cm Grade Count:34
Spiral Flow 48.0 - 180 cm
18.9 - 70.9 in
Average value: 107 cm Grade Count:52
Ash 71.4 - 88.6 %
71.4 - 88.6 %
Average value: 79.3 % Grade Count:37
Mechanical Properties Metric English Comments
Hardness, Shore D 55.0 - 86.0
55.0 - 86.0
Average value: 76.1 Grade Count:55
Tensile Strength, Ultimate 13.8 - 300 MPa
2000 - 43500 psi
Average value: 89.6 MPa Grade Count:23
80.0 - 123 MPa

@Temperature 150 - 250 °C
11600 - 17800 psi

@Temperature 302 - 482 °F
Average value: 97.0 MPa Grade Count:2
Elongation at Break 0.300 - 2.00 %
0.300 - 2.00 %
Average value: 0.780 % Grade Count:10
0.300 - 0.700 %

@Temperature 150 - 250 °C
0.300 - 0.700 %

@Temperature 302 - 482 °F
Average value: 0.500 % Grade Count:2
Modulus of Elasticity 1.38 - 46.0 GPa
200 - 6670 ksi
Average value: 19.2 GPa Grade Count:16
14.0 - 32.0 GPa

@Temperature 150 - 250 °C
2030 - 4640 ksi

@Temperature 302 - 482 °F
Average value: 23.3 GPa Grade Count:2
Flexural Yield Strength 35.5 - 400 MPa
5150 - 58000 psi
Average value: 134 MPa Grade Count:70
6.86442 - 345 MPa

@Temperature 150 - 260 °C
995.602 - 50000 psi

@Temperature 302 - 500 °F
Average value: 58.4 MPa Grade Count:28
Flexural Modulus 2.41 - 32.0 GPa
349 - 4640 ksi
Average value: 16.6 GPa Grade Count:67
0.686465 - 30.0 GPa

@Temperature 150 - 260 °C
99.5649 - 4350 ksi

@Temperature 302 - 500 °F
Average value: 6.87 GPa Grade Count:28
Compressive Yield Strength 6.89 - 350 MPa
1000 - 50800 psi
Average value: 161 MPa Grade Count:21
127 - 219 MPa

@Temperature 150 - 250 °C
18400 - 31800 psi

@Temperature 302 - 482 °F
Average value: 172 MPa Grade Count:2
Compressive Modulus 1.03 - 35.0 GPa
150 - 5080 ksi
Average value: 8.95 GPa Grade Count:5
Adhesive Bond Strength 8.96 - 15.9 MPa
1300 - 2310 psi
Average value: 11.7 MPa Grade Count:3
13.8 - 15.9 MPa

@Temperature -55.0 - 93.0 °C
2000 - 2310 psi

@Temperature -67.0 - 199 °F
Average value: 14.9 MPa Grade Count:1
Izod Impact, Notched 0.299 - 21.0 J/cm
0.560 - 39.3 ft-lb/in
Average value: 10.9 J/cm Grade Count:4
Charpy Impact Unnotched 0.200 - 0.900 J/cm²
0.952 - 4.28 ft-lb/in²
Average value: 0.590 J/cm² Grade Count:5
Charpy Impact, Notched 0.150 - 5.40 J/cm²
0.714 - 25.7 ft-lb/in²
Average value: 2.85 J/cm² Grade Count:12
Thermal Properties Metric English Comments
CTE, linear 3.30 - 80.0 µm/m-°C
1.83 - 44.4 µin/in-°F
Average value: 31.4 µm/m-°C Grade Count:59
15.0 - 25.0 µm/m-°C

@Temperature 50.0 - 150 °C
8.33 - 13.9 µin/in-°F

@Temperature 122 - 302 °F
Average value: 19.2 µm/m-°C Grade Count:3
CTE, linear, Transverse to Flow 40.0 - 80.0 µm/m-°C
22.2 - 44.4 µin/in-°F
Average value: 59.3 µm/m-°C Grade Count:21
Thermal Conductivity 0.400 - 1.34 W/m-K
2.78 - 9.30 BTU-in/hr-ft²-°F
Average value: 0.731 W/m-K Grade Count:54
Maximum Service Temperature, Air 93.0 - 250 °C
199 - 482 °F
Average value: 178 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 149 - 243 °C
300 - 469 °F
Average value: 211 °C Grade Count:7
Deflection Temperature at 8.0 MPa 115 - 180 °C
239 - 356 °F
Average value: 144 °C Grade Count:5
Glass Transition Temp, Tg 75.0 - 275 °C
167 - 527 °F
Average value: 178 °C Grade Count:63
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:55
Oxygen Index 28.0 - 34.0 %
28.0 - 34.0 %
Average value: 31.8 % Grade Count:18
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 5.60e+16 ohm-cm
1.00e+12 - 5.60e+16 ohm-cm
Average value: 9.96e+15 ohm-cm Grade Count:45
1.00e+9 - 3.20e+12 ohm-cm

@Temperature 150 - 150 °C
1.00e+9 - 3.20e+12 ohm-cm

@Temperature 302 - 302 °F
Average value: 1.03e+12 ohm-cm Grade Count:8
Surface Resistance 1.00e+12 - 1.00e+15 ohm
1.00e+12 - 1.00e+15 ohm
Average value: 2.31e+14 ohm Grade Count:5
Dielectric Constant 3.13 - 7.00
3.13 - 7.00
Average value: 3.93 Grade Count:52
Dielectric Strength 1.40 - 55.1 kV/mm
35.6 - 1400 kV/in
Average value: 22.9 kV/mm Grade Count:55
Dissipation Factor 0.000300 - 0.0500
0.000300 - 0.0500
Average value: 0.00748 Grade Count:41
Arc Resistance 180 - 240 sec
180 - 240 sec
Average value: 185 sec Grade Count:23
Comparative Tracking Index 225 - 600 V
225 - 600 V
Average value: 378 V Grade Count:9
Processing Properties Metric English Comments
Processing Temperature 135 - 193 °C
275 - 379 °F
Average value: 172 °C Grade Count:18
Mold Temperature 160 - 190 °C
320 - 374 °F
Average value: 175 °C Grade Count:39
Cycle Time - Injection 30.0 - 150 sec
30.0 - 150 sec
Average value: 82.0 sec Grade Count:5
Cure Time 0.250 - 10100 min
0.00417 - 168 hour
Average value: 489 min Grade Count:28