Techmer ES PlastiblendÂ® PA6/6,6 GF60 HS L 60% Glass Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 60% Glass Fiber Reinforced
Manufacturer	Techmer ES
Trade Name	Plastiblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES PlastiblendÂ® PA6/6,6 GF60 HS L 60% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized, Copolymer and LubricatedAppearance: BlackProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.70 g/cc	0.0614 lb/inÂ³	ASTM D792
Water Absorption	0.35 % @Time 86400 sec	0.35 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Thickness 3.17 mm	0.0030 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	121	121	ASTM D785
Tensile Strength, Yield	241 MPa	35000 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Yield Strength	352 MPa	51000 psi	ASTM D790
Flexural Modulus	1.76 GPa	255 ksi	ASTM D790
Izod Impact, Notched	1.87 J/cm @Thickness 3.17 mm	3.50 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	12.6 Âµm/m-Â°C	7.00 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	257 Â°C	495 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	241 Â°C	465 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Strength	18.9 kV/mm	480 kV/in	Method A (Short-Time); ASTM D149