Ovation Polymers Nima™ NH PA66UT Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Ovation Polymers
Trade Name Nima™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ovation Polymers Nima™ NH PA66UT Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM standards. Variations within normal tolerances are possible for various types of colors and functional properties like UV resistance.Information provided by Ovation Polymers
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage 0.011 - 0.0125 cm/cm

@Thickness 3.17 mm
0.011 - 0.0125 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.0035 - 0.0060 cm/cm

@Thickness 3.17 mm
0.0035 - 0.0060 in/in

@Thickness 0.125 in
Melt Index of Compound 4.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 38.0 MPa
5510 psi
50 mm/min; ASTM D638
Elongation at Break 20 %
20 %
50 mm/min; ASTM D638
Tensile Modulus 1.40 GPa
203 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 55.0 MPa
7980 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.70 GPa
247 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.869 J/cm
3.501 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 73.0 °C

@Thickness 3.20 mm
163 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C

@Thickness 3.20 mm
136 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0
V-0