North Wood Plastics PS with 20% Wood Fiber
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Wood Filled |
| Manufacturer | North Wood Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | North Wood Plastics PS with 20% Wood Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by North Wood Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.074 g/cc | 0.03880 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0026 cm/cm | 0.0026 in/in | ASTM D955 |
| Melt Flow | 1.6 g/10 min @Temperature 190 °C |
1.6 g/10 min @Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Elongation at Break | 5.8 % | 5.8 % | ASTM D638 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ASTM D638 |
| Flexural Yield Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 0.410 J/cm | 0.768 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 200 °C | <= 392 °F | To prevent fiber degradation. |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 190 CLEAR FLEXIBLE (4000 Viscosity) Rapid Bonding Adhesive
- NOVA Chemicals Sclair® 11D1 Butene LLDPE Film Resin (discontinued **)
- Kolon KOPA® KN135HB40SIBL Multi Reinforced Nylon 6
- Haynes 25 alloy, cold worked sheet, 15 % cold reduction
- SABIC Innovative Plastics Valox® IQ4860HR PBT (Europe-Africa-Middle East)
- DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66 (Unverified Data**)
- CMT Materials REN Shape® 5169 Foundry Pattern Board
- Carmel Olefins CAPILENE® G 65 F Polypropylene Homopolymer
- Arlon R30711R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved