- Nilit RECONYL A GV30 Recycled nylon 6.6 for injection molding, 30% glass fiber reinforced
Nilit RECONYL A GV30 Recycled nylon 6.6 for injection molding, 30% glass fiber reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL A GV30 Recycled nylon 6.6 for injection molding, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6.6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.4 - 2.4 % | 1.4 - 2.4 % | ISO 62 |
| Water Absorption at Saturation | 5.5 - 6.5 % | 5.5 - 6.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.023 cm/cm | 0.0040 - 0.023 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 174 MPa | 25200 psi | ISO 2039-1 |
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.40 J/cm² | 16.2 ft-lb/in² | DIN 53453 |
| 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | |
| 2.80 J/cm² @Temperature -40.0 °C |
13.3 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
Users viewing this material also viewed the following:
- Nye Lubricants 731 (IG) Synthetic Oil
- Polykemi AB SCANMID 6 B12^ F25 Nylon 6, Glass Fiber Reinforced
- Permabond TA435 Toughened Acrylic Adhesive & Initiator
- LATI Latamid 6 H-V0 PA 6, Heat Stabilized, Flame Retardant
- Solvay Specialty Polymers Amodel® FC-1150 Polyphthalamide (PPA), 50% Glass Fiber
- Sichuan Deyang Haton® hFR81 Polyphenylene Sulfide
- Tipco Tipcolite® TMS 211 Phenolic Compound, Cotton, Filler & Wood Flour, having Medium Flow & High Strength
- Eastman Tenite Butyrate 485A2R30016 Natural Cellulose Acetate Butyrate
- Covestro Makrolon® LTG3123 Polycarbonate
- Eastman VersaTray 12822 Plastic (discontinued **)
Copyright © lookpolymers.com All Rights Reserved