 POLYMER SEARCH

Formosa Plastics Formolene® E927 Film HDPE

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® E927 Film HDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Density Polyethylene High Molecular Weight Bi-Modal Resin For Thin Film Applications Formolene® E927 is a high molecular weight grade of HDPE designed for high drawdown to produce thin films with good processing and physical properties. Formolene® E927 is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Formolene® E927 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Multi-Wall Bag Liners, T-Shirt Bags, Merchandise Bags, Trash Can Liner and Heavy Duty BagsInformation provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.949 g/cc
0.0343 lb/in³
ASTM D1505
Thickness 15.2 microns
0.600 mil
Melt Flow 0.070 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.070 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
High Load Melt Index 12 g/10 min

@Load 21.6 kg,
Temperature 190 °C
12 g/10 min

@Load 47.6 lb,
Temperature 374 °F
Condition F; ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 280 %
280 %
ASTM D882
Film Elongation at Break, TD 410 %
410 %
ASTM D882
Elmendorf Tear Strength MD 11 g
11 g
ASTM D1922
Elmendorf Tear Strength TD 60 g
60 g
ASTM D1922
Dart Drop Test 380 g
0.838 lb
ASTM D1709
Film Tensile Strength at Break, MD 57.2 MPa
8300 psi
ASTM D882
Film Tensile Strength at Break, TD 49.6 MPa
7200 psi
ASTM D882
1% Secant Modulus, MD 814 MPa
118000 psi
ASTM D882
1% Secant Modulus, TD 1010 MPa
146000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 131 °C
268 °F
DSC
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 4.0
4.0