POLYMER SEARCH

Nilit Nilamid A3 H G10 50% Glass Reinforced PA66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer	Nilit
Trade Name	Nilamid
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nilit Nilamid A3 H G10 50% Glass Reinforced PA66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance, even at elevated temperatures. It is used for highly loaded applications like high torque transmission housings, electrical cable holders and tensioners of ski bindings.Key characteristics: High stiffnessHigh strengthGood impact strength Excellent thermal performanceGood creep resistanceInformation provided by NILIT.

Physical Properties	Metric	English	Comments
Density	1.57 g/cc	0.0567 lb/in³	ASTM D792, ISO 1183
Water Absorption	0.50 %	0.50 %	23°C, 24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation	3.5 %	3.5 %	sim. ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm	0.0020 in/in	Euronil
Linear Mold Shrinkage, Transverse	0.0030 cm/cm	0.0030 in/in	Euronil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	220 MPa	31900 psi	ISO 527, ASTM D638
Elongation at Break	2.0 %	2.0 %	ISO 527, ASTM D638
Tensile Modulus	16.5 GPa	2390 ksi	ISO 527, ASTM D638
Flexural Yield Strength	310 MPa	45000 psi	ISO 178, ASTM D790
	230 MPa @Temperature 90.0 °C	33400 psi @Temperature 194 °F	ISO 178, ASTM D790
Flexural Modulus	15.0 GPa	2180 ksi	ISO 178, ASTM D790
	9.50 GPa @Temperature 90.0 °C	1380 ksi @Temperature 194 °F	ISO 178, ASTM D790
Izod Impact, Notched (ISO)	13.0 kJ/m² @Temperature -30.0 °C	6.19 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
	16.0 kJ/m² @Temperature 23.0 °C	7.61 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	7.00 J/cm²	33.3 ft-lb/in²	ISO 179
	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	1.60 J/cm²	7.61 ft-lb/in²	ISO 179
	1.30 J/cm² @Temperature -30.0 °C	6.19 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	115 °C	239 °F	20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi)	262 °C	504 °F	ISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	257 °C	495 °F	ISO 75, ASTM D648
Vicat Softening Point	257 °C	495 °F	49 N; ISO 306, ASTM D1525
	260 °C	500 °F	9.8 N; ISO 306, ASTM D1525
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in
	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in
Oxygen Index	27 %	27 %	ASTM D2863
Glow Wire Test	650 °C @Thickness 3.20 mm	1200 °F @Thickness 0.126 in	Glow Wire Flammability Index; IEC 694-2-12
	650 °C @Thickness 0.800 mm	1200 °F @Thickness 0.0315 in	Glow Wire Flammability Index; IEC 694-2-12

Electrical Properties	Metric	English	Comments
Dielectric Strength	22.0 kV/mm @Thickness 2.00 mm	559 kV/in @Thickness 0.0787 in	ASTM D149
Comparative Tracking Index	350 V @Thickness 3.20 mm	350 V @Thickness 0.126 in	Sol. B; IEC 112, UL 746A
	500 V @Thickness 3.20 mm	500 V @Thickness 0.126 in	Sol. A; IEC 112, UL 746A

Processing Properties	Metric	English	Comments
Nozzle Temperature	285 - 300 °C	545 - 572 °F
Zone 1	270 - 290 °C	518 - 554 °F	hopper
Zone 2	275 - 290 °C	527 - 554 °F
Zone 3	285 - 300 °C	545 - 572 °F
Zone 4	285 - 300 °C	545 - 572 °F
Melt Temperature	280 - 300 °C	536 - 572 °F	Do not melt above 300°C
Mold Temperature	100 - 120 °C	212 - 248 °F	Preferred
Drying Temperature	80.0 - 85.0 °C	176 - 185 °F
Dry Time	4 hour	4 hour
Injection Pressure	70.0 - 100 MPa	10200 - 14500 psi

Descriptive Properties	Value	Comments
Clamping Force	in tons, 0.7 times the projected surface area in cm²
Flammability Rating	B28	FMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball Test	OK	at 125°C, IEC 309
	OK	at 165°C, IEC 309
Holding Pressure	90 Mpa

Users viewing this material also viewed the following: