Nilit FRIANYL C73 TFGV1530 Nylon 6.6/6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL C73 TFGV1530 Nylon 6.6/6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 - 1.5 % | 0.50 - 1.5 % | ISO 62 |
| Water Absorption at Saturation | 3.5 - 4.5 % | 3.5 - 4.5 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.013 cm/cm | 0.0050 - 0.013 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 169 MPa | 24500 psi | ISO 2039-1 |
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 10.44 GPa | 1514 ksi | ISO 527 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.10 J/cm² | 19.5 ft-lb/in² | DIN 53453 |
| 3.70 J/cm² @Temperature -40.0 °C |
17.6 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Radici Heraflex® E 4718 TPC-ET Thermoplastic Elastomer
- Lord Adhesives Metech 3505 Palladium Silver Conductor Composition
- Solvay TECHNYLSTARâ„¢ S 218 V35 PA6, 35% glass filled, DRY
- Techmer ES Luriblend® PA6 CF30 TL15 BK 30% Carbon Filled
- Master Bond MasterSil 705C Non-Corrosive Silicone with Carbon Filler
- EMS-Grivory Grivory® BG-30 FR PA6-GF30 FR
- Epoxy Technology EPO-TEK® 301-2 Optically Transparent Epoxy
- Dow Nordel® IP 4640 Molded Golf Grips
- Austin Novel Materials Texalan® 265A Polyester-based TPU
Copyright © lookpolymers.com All Rights Reserved